报告题目：Controlling the Energy Structure of AgInGaS Quantum Dots for Enhancing Their Photoluminescence Property and Photocatalytic Activity

报告时间：2022年9月23日上午10:00-11:30

报告地点：腾讯会议

会议ID: 578-702-581

报 告 人：Prof. Tsukasa Torimoto（教授、名古屋大学）

报告主持人：Prof. Masakazu Ampo（教授、beat365正版唯一官网&日本大阪公立大学）

报告摘要:

Quantum dots (QDs) composed of group I-III-VI semiconductors, such as CuInS₂ and AgInS₂, exhibit unique size- and composition-dependent physicochemical properties different from bulk materials due to the quantum size effect. Furthermore, these QDs have attracted intense attention for developing highly efficient solar energy conversion systems, because of the less toxicity and the large absorption coefficients in visible and near-IR regions. Recently we have successfully prepared alloy QDs composed of ZnAgInS or ZnAgInSe semiconductors.^(1,2) Their photocatalytic H₂ evolution activity was controlled by the chemical composition and size of QDs. On the other hand, the E_g of bulk I-III-VI semiconductors can be controlled by alloying different metal cations of group III elements. In this lecture, I introduce the preparation of less-toxic AgIn_(1-x)Ga_xS₂ (AIGS(x)) alloy QDs and their photoluminescence (PL) property and photocatalytic activity for H₂ evolution.

AIGS(x) QDs with different x values were synthesized by thermal decomposition of Ag(OAc), In(acac)₃, Ga(acac)₃, and S powders in a mixture solution of oleylamine and dodecanethiol (DDT). The composition of resulting QDs, that is, x value, was controlled by varying the Ga/(In+Ga) ratio in preparation. Thus-obtained AIGS QDs were surface-coated with GaS_x or ZnS shells, resulting in the formation of core-shell-structured QDs, AIGS(x)@GaS_x or AIGS(x)@ZnS. The surface modifiers on QDs were changed from DDT to mercaptopropionic acid (MPA) for photocatalytic H₂ evolution in an aqueous solution.

Fig. 1 PL spectra of AIGS@GaS_x QDs and photographs of solutions containing AIGS and AIGS@GaS_x QDs

The obtained AIGS(x) QDs had a spherical shape with size of ca. 4 nm. AIGS(x) QDs exhibited a sharp band-edge PL peak as well as a broad defect-site emission.⁽³⁾ The peak wavelength of the band edge emission was tunable from 610 to 500 nm with an increase in the x value as a result of an increase of the E_g. The surface coating of AIGS(x) with GaS_x shell drastically and selectively suppressed the broad defect-site PL peak (Fig. 1) and, at the same time, led to an increase in the PL quantum yield (QY) of the band edge emission peak. The optimal PL QY was 28% for AIGS(x)@GaS_x QDs with green band-edge emission at 530 nm and a full width at half-maximum of 181 meV (41 nm).

ZnS shells of 0~ 2 nm in thickness were coated on AIGS(x) QDs for photocatalytic H₂ evolution. The irradiation to AIGS(x)@ZnS QDs suspended in an aqueous solution containing Na₂S as a hole scavenger was carried out using Xe lamp light (λ> 350 nm). With the elapse of light irradiation, the amount of H₂ evolved linearly increased, regardless of the composition of AIGS core or the ZnS shell thickness. The H₂ evolution rate was remarkably dependent on the composition of AIGS core. The highest photocatalytic activity was obtained for AIGS(x)@ZnS QDs with x=0.6 and the ZnS shell thickness of ca. 2 nm. These behavior can be explained by the changes in the stability of AIGS core in aqueous solutions, the conduction band level of QDs, and the amount of photon absorption.

References: (1) T. Kameyama, et al., J. Phys. Chem. C 2015, 119, 24740-24749. (3) P.-Y. Hsieh, et al., J. Mater. Chem. A 2020, 8, 13142-13149. (3) T. Kameyama, et al., ACS Appl. Mater. Interfaces 2018, 10, 42844−42855.